LEI Wen,YANG Tao,XU Jin-bao,et al.Preparation of Bio-Adhesive Based on Soybean via Co-polymerization Method[J].Soybean Science,2010,29(02):299-301,305.[doi:10.11861/j.issn.1000-9841.2010.02.0299]
共聚改性大豆蛋白制备胶粘剂的研究
- Title:
- Preparation of Bio-Adhesive Based on Soybean via Co-polymerization Method
- 文章编号:
- 1000-9841(2010)02-0299-03
- 分类号:
- TQ432.7
- 文献标志码:
- A
- 摘要:
- 采用改性剂MF处理大豆蛋白(SPI),用马来酸酐(MA)接枝改性后,与苯乙烯(St)发生共聚制备胶粘剂,研究了配方及反应温度对胶粘剂耐水胶接强度及粘度的影响。增加SPI的用量,胶粘剂的粘度将逐渐增大,耐水胶合强度起初增加迅速,之后增加趋势变缓;增加改性剂的用量,胶粘剂粘度与耐水胶合强度都呈先下降后上升趋势;当MA用量为1.5 g时,胶粘剂的粘度最小,而用量为4.5 g时,胶粘剂的粘度最大,随着MA用量的增加,胶粘剂耐水胶合强度先上升而后大幅下降;St用量对胶粘剂粘度的影响较复杂,但耐水胶合强度却随着St用量的增加先上升后下降,当St用量为20 mL时,耐水胶合强度达到最大值2.78 MPa;当引发剂的量为0.05 g(1mL苯乙烯)时,胶粘剂的耐水胶合强度出现最大值2.79 MPa,且此时粘度仅为12 MPa·S,对施胶影响不大。最终确定最佳反应条件为:SPI 15 g、MF 6.5%(相对于SPI)、MA 3.0 g,St 20 mL, 引发剂0.05 g(1 mL St用量),反应温度70°C。
- Abstract:
- After being treated with modifier (MF),the soy protein was grafted with maleic anhydride(MA),and then co-polymerized with styrene(St) to prepare bio-adhesive,the original viscosity and its water-resistant bonding strength(WRBS) of the adhesive were investigated respectively,the optimal synthesis conditions are concluded as: 15g SPI, 6.5%(compared with that of SPI) MF, 3.0 g MA, 20 mL St, 0.05g/(1mL St)initiator,reaction temperature 70°C。With the increase of the dosage of SPI,the viscosity of the adhesive will be accordingly increased and WRBS increases dramatically at first and then slowly;increasing the dosage of the modifier will make both the viscosity and WRBS decrese first and then increase;when 1.5g MA is added,the adhesive has the least viscosity ,while it has the most one when 4.5g MA is used,WRBS of the adhesive will increase first and then decrease dramatically with the increasing dosage of MA;though the effect of the dosage of St on the viscosity of the adhesive is complicated,the adhesive will have the greatest WRBS of 2.78 MPa when 20 mL St is used;as the initiator is regarded,0.05g initiator in 1mL St makes the viscosity have the greatest WRBS of 2.79 MPa,and the viscosity is only 12MPa·S in this situation,which has little effect on the coating process.
参考文献/References:
[1]Kumar R, Choudhary V, Mishra S,et al. Adhesives and plastics based on soy protein products[J]. Industrial Crops and Products, 2002, 16:155-172. [2]Mo X Q, Cheng E Z, Wang D H,et al. Physical properties of medium-density wheat straw particleboard using different adhesives[J]. Industrial Crops and Products, 2003,(18)1: 47-53. [3]Huang W N,Sun X Z. Adhesive properties of soy proteins modified by urea and guanidine hydrochloride[J]. Journal of the American Oil Chemists’ Society,2000,77(1):101-104. [4]雷文,杨涛,景露,等.利用大豆分离蛋白制备胶粘剂[J].大豆科学,2009,28(4):715-718.(Lei W,Yang T,Jing L,et al.Preparation of adhesives from soy protein isolate[J].Soybean Science, 2009,28(4):715-718.) [5]Huang J,Li K. A new soy flour-based adhesive for making interior type II plywood[J]. Journal of the American Oil Chemists’ Society,2008,85(1):63-70. [6]奚冬雷.大豆分离蛋白接枝改性及应用研究[D].无锡:江南大学,2005:2-22.(Xi D L. Study on the gafted modification and application of soy protein isolate[D].Wuxi:Jiangnan University, 2005:2-22.) [7]陈贻文. 有机仪器分析[M]. 长沙:湖南大学出版社,1999:262-330.(Chen Y W.Analysis by organic instruments[M].Changsha:Hunan University Press, 1999:262-330.)
相似文献/References:
[1]郑荣生,张波,童军茂,等.三种市售大豆蛋白产品理化特性研究[J].大豆科学,2013,32(01):84.[doi:10.3969/j.issn.1000-9841.2013.01.020]
ZHENG Rong-sheng,ZHANG Bo,TONG Jun-mao,et al.Physicochemical Properties of Three Kinds of Commercial Soybean Protein Products[J].Soybean Science,2013,32(02):84.[doi:10.3969/j.issn.1000-9841.2013.01.020]
[2]黄橙子,王静,高红亮,等.酶法提高大豆分离蛋白酸溶性的研究[J].大豆科学,2013,32(01):111.[doi:10.3969/j.issn.1000-9841.2013.01.026]
HUANG Cheng-zi,WANG Jing,GAO Hong-liang,et al.Improvement on Acid-solubility of Soy Protein Isolate with Enzymatic Method[J].Soybean Science,2013,32(02):111.[doi:10.3969/j.issn.1000-9841.2013.01.026]
[3]葛文静,华欲飞.低限度酶解制备低粘度弱苦味的大豆分离蛋白[J].大豆科学,2014,33(01):114.[doi:10.11861/j.issn.1000-9841.2014.01.0114]
GE Wenjing,HUA Yufei.Limited Enzymatic Hydrolysis of Soybean Protein Isolates to Obtain Hydrolysate with Lower Viscosity and Weaker Bitterness[J].Soybean Science,2014,33(02):114.[doi:10.11861/j.issn.1000-9841.2014.01.0114]
[4]孟 滕,刘丹丹,李海云,等.可食性复合膜制备工艺的研究[J].大豆科学,2014,33(02):277.[doi:10.11861/j.issn.1000-9841.2014.02.0277]
MENG Teng,LIU Dan-dan,LI Hai-yun,et al.Processing Technology of Edible Composite Membranes[J].Soybean Science,2014,33(02):277.[doi:10.11861/j.issn.1000-9841.2014.02.0277]
[5]刘 莹,刘 政,赵 杰,等.超声波辅助酶法制备大豆抗氧化肽[J].大豆科学,2014,33(02):281.[doi:10.11861/j.issn.1000-9841.2014.02.0281]
LIU Ying,LIU Zheng,ZHAO Jie,et al.Preparation of Soybean Antioxidant Peptide by Ultrasonic-assisted Enzymatic Method[J].Soybean Science,2014,33(02):281.[doi:10.11861/j.issn.1000-9841.2014.02.0281]
[6]胡少新,江连洲,许德春,等.大豆分离蛋白生产降血压肽酶解技术研究[J].大豆科学,2011,30(04):643.[doi:10.11861/j.issn.1000-9841.2011.04.0643]
HU Shao-xin,JIANG Lian-zhou,XU De-chun,et al.Producing Technology of Antihypertensive Peptide Derived from Soybean Protein Isolated by Enzymatic Method[J].Soybean Science,2011,30(02):643.[doi:10.11861/j.issn.1000-9841.2011.04.0643]
[7]闫 晗,聂简琪,葛佩富,等.速溶性大豆分离蛋白生产工艺优化[J].大豆科学,2012,31(06):996.[doi:10.3969/j.issn.1000-9841.2012.06.030]
YAN Han,NIE Jian-qi,GE Pei-fu,et al.Optimization on Production Parameters of Rapid Dissolving Soybean Protein Isolate[J].Soybean Science,2012,31(02):996.[doi:10.3969/j.issn.1000-9841.2012.06.030]
[8]雷文.国内大豆胶粘剂的改性研究进展[J].大豆科学,2011,30(02):328.[doi:10.11861/j.issn.1000-9841.2011.02.0328]
LEI Wen.Domestic Research on Soybean Adhesives Modification[J].Soybean Science,2011,30(02):328.[doi:10.11861/j.issn.1000-9841.2011.02.0328]
[9]王玲琴,王志耕,方玉明,等.双酶法制备大豆降胆固醇活性肽的研究[J].大豆科学,2010,29(01):109.[doi:10.11861/j.issn.1000-9841.2010.01.0109]
WANG Ling-qin,WANG Zhi-geng,FANG Yu-ming,et al.Preparation of Soybean Hypocholesterolemic Peptides by Double-protease Method[J].Soybean Science,2010,29(02):109.[doi:10.11861/j.issn.1000-9841.2010.01.0109]
[10]雷文,杨涛,王考将,等.环氧树脂改性大豆基木材胶粘剂的制备与表征[J].大豆科学,2010,29(01):118.[doi:10.11861/j.issn.1000-9841.2010.01.0118]
LEI Wen,YANG Tao,WANG Kao-jiang,et al.Preparation and Characterization of Bio-adhesive by Modifying Soy Protein Isolate with Epoxy Resin[J].Soybean Science,2010,29(02):118.[doi:10.11861/j.issn.1000-9841.2010.01.0118]
备注/Memo
基金项目:江苏省高校大学生实践创新资助项目(苏教高〔2009〕30号),南京林业大学大学生科技创新资助项目(200951,200994)。